Hydrothermal Synthesis of CuO Micro/Nanoparticles and Their Application in Gas Sensors
作者:
胡校兵; 谢祯芳; 谢骥; 解丽丽; 朱志刚
上海第二工业大学 环境与材料工程学院,上海,201209
Author(s):
Hu Xiaobing;  Xie Zhenfang;  Xie Ji;  Xie Lili;  Zhu Zhigang
School of Environment and Materials Engineering, Shanghai Second University of Technology, Shanghai, 201209
关键词:
气体传感器; 氧化铜颗粒; 水热法; 掺杂
Keywords:
DOI:
10.13705/j.issn.1671-6833.2016.03.022
文献标志码:
A
摘要:
以硝酸铜( Cu( NO3)2)为原料,以六次甲基四胺( C6 H12 N4)为模板剂,采用水热合成法制备CuO微纳米颗粒,通过扫描电镜和X射线衍射仪对产物的组成及形貌进行表征,并将合成粉体制备成敏感膜,通过静态配气法对产物气敏性能进行研究.结果表明：在硝酸铜和六次甲基四胺的摩尔比为1∶45,水热温度为110℃的条件下,制备出粒径1~2μm大小的纺锤状氧化铜粉体,其中纺锤结构是由100 nm左右的纳米片组成.另外,纳米氧化铜对丙酮( CH3 COCH3)和硫化氢( H2 S)气体有较好的选择性,进一步掺杂0.25%~1.25%的贵金属催化剂铂(Pt)后,氧化铜对硫化氢显示出了良好的选择性,且灵敏度有一定程度的提高.
Abstract:
Micro/Nano-particles of CuO were prepared with hexamethylenetetramine template. The composi-tion and morphology of the product were characterized by SEM and X-ray diffraction. The synthetic powder was prepared as sensitive membrane, and its gas sensitivity was studied with a static gas distribution method. The results indicated that the uniform copper oxide powders was synthesized at the 110℃, and the molar ratio be-tween copper nitrate and hexamethylenetetramine was 1∶45. The spindle structure was around 1~2 μm, and was composed of 100 nm nanoplates. The sensor had better selectivity with CH3 COCH3 and H2 S. Copper ox-ide showed good selectivity to hydrogen sulfide and its sensitivity had a certain degree of improvement after fur-ther doping 0. 25% ~1. 25% noble metal catalyst Pt.

相似文献/References:

[1]陈杨,李志鑫,段智明,等.基于聚酰胺树枝状分子的QCM甲醛传感器研究[J].郑州大学学报(工学版),2016,37(04):36.[doi:10.13705/j.issn.1671-6833.2016.04.008]
　Chen Yang,Li Zhixin,Duan Zhiming,et al.Research On The QCM Formaldehyde Sensor Based On Polyamide Dendrimers[J].Journal of Zhengzhou University (Engineering Science),2016,37(06):36.[doi:10.13705/j.issn.1671-6833.2016.04.008]
[2]李娜,向群,程知萱,等.多孔SnO2空心球材料的合成及甲醛气敏性能研究[J].郑州大学学报(工学版),2019,40(06):27.[doi:10.13705/j.issn.1671-6833.2019.06.004]
　Li Na,Xiang Qun,Cheng Zhixuan,et al.Synthesis of Porous SnO2 Hollow Sphere and Gas Sensing Properties of Formaldehyde[J].Journal of Zhengzhou University (Engineering Science),2019,40(06):27.[doi:10.13705/j.issn.1671-6833.2019.06.004]
[3]曹晨璐,高健.Pd掺杂ZnO材料的制备及其对NO2气敏性能研究[J].郑州大学学报(工学版),2019,40(06):38.[doi:10.13705/j.issn.1671-6833.2019.06.012]
　Cao Chenlu,Cao Chunmei,Guo Meiyuan,et al.Synthesis, Characterization and Nitrogen Dioxide Gas Sensing Applications of Pd Doped ZnO Semiconductor Material[J].Journal of Zhengzhou University (Engineering Science),2019,40(06):38.[doi:10.13705/j.issn.1671-6833.2019.06.012]

更新日期/Last Update: