Title:
Estimation of the fatigue life of the T -type tube welding node
作者:
束继兴;沈怡民;丁遂栋;
上海交通大学,郑州工学院,郑州工学院,
Author(s):
Shu Jixing; Shen Yimin; Ding Suidong;
Shanghai Jiaotong University, Zhengzhou Institute of Technology, Zhengzhou Institute of Technology,
关键词:
裂纹; 断裂; 疲劳寿命; 应力强度因子
Keywords:
Crack;  Fracture;  fatigue life;  stress strength factor
文献标志码:
A
摘要:
本文用固有缺陷法推导出估算T型管焊节点疲劳寿命的有关公式,并将计算结果与试验值进行比较,还提供了一些可供应用的曲线.
Abstract:
This article uses the inherent defect method to derive the relevant formula of the fatigue life of the T -shaped tube welding node, and compare the calculation results with the test value. It also provides some applied curves.

相似文献/References:

[1]闫安志,陶天增,张振华.端部质量对有无损伤悬臂梁的模态影响分析[J].郑州大学学报(工学版),2016,37(05):39.[doi:10.13705/j.issn.1671-6833.2016.05.008]
　Yan Anzhi,Tao Tianzeng,Zhang Zhenhua.The mode analysis of the cantilever beam with concentrated mass on its free end in the case of with and without damage[J].Journal of Zhengzhou University (Engineering Science),2016,37(02):39.[doi:10.13705/j.issn.1671-6833.2016.05.008]
[2]张军,李志宏,贾宏.五层粘接结构的断裂行为模拟研究[J].郑州大学学报(工学版),2017,38(01):22.[doi:10.13705/j.issn.1671-6833.2017.01.001]
　Zhang Jun,Li Zhihong,Jia Hong.Investigation on Interface and Adhesive Layer Fracture Characteristic of Adhesively Bonded Joints[J].Journal of Zhengzhou University (Engineering Science),2017,38(02):22.[doi:10.13705/j.issn.1671-6833.2017.01.001]
[3]杜云海,王志,候建华..裂纹问题超奇异积分方程法的程序实现[J].郑州大学学报(工学版),2013,34(04):124.[doi:10.3969/j.issn.1671-6833.2013.04.029]
　DU Yun-hai,WANG Zhi,HOU Jian-hua.Programming on Hyper-singular Integral Equation Method for Crack[J].Journal of Zhengzhou University (Engineering Science),2013,34(02):124.[doi:10.3969/j.issn.1671-6833.2013.04.029]
[4]王爱珍.全奥氏体钢焊缝金属的显微裂纹[J].郑州大学学报(工学版),1995,16(01):93.
　Wang Aizhen.Micro cracks of all Olympic Steel Weld Metals[J].Journal of Zhengzhou University (Engineering Science),1995,16(02):93.
[5]董耀星,周鸿钧,王博,等.弹性地基上重力坝坝踵界面裂缝断裂可靠度分析[J].郑州大学学报(工学版),1992,13(03):7.
　Dong Yaoxing,Zhou Hongjun,Wang Bo,et al.Analysis of reliability analysis of elastic base gravity dam and damage interface fracture reliability analysis[J].Journal of Zhengzhou University (Engineering Science),1992,13(02):7.
[6]丁遂栋.无限大板中心裂纹应力强度因子[J].郑州大学学报(工学版),1987,8(01):39.
　[J].Journal of Zhengzhou University (Engineering Science),1987,8(02):39.

更新日期/Last Update: 1900-01-01